刘飞,郭子如,张阳
LIU Fei,GUO Zi-ru,ZHANG Yang

• 1:安徽理工大学化学工程学院

摘要(Abstract)：

在组分和制备工艺完全一致的情况下,研究了添加新型纳米级HL抗冻剂对水胶炸药抗冻性能的影响作用。将水胶炸药试验样品在-20℃下冷冻24小时后测试其作功能力,用作功能力大小表征试样的抗冻性能。对比了水胶炸药试样添加该抗冻剂前后的抗冻性能,研究了添加不同量的抗冻剂对水胶炸药试样抗冻性能的影响。结果表明,在该抗冻剂添加量达到4%之后,水胶炸药的抗冻性能得到明显提高,且随着该抗冻剂添加量的增加水胶炸药的抗冻性能先增后降,呈现出近似抛物线型变化趋势,其最佳添加量为8%~9%。
Under completely identical condition of the water-gel explosive component and preparation process,the impact of the new nano-HL antifreeze agent on the frost-resistance of the water-gel explosive was studied.The working capacity of the water-gel explosive samples were tested after frozen 24 hours in-20℃,the frost-resistance was characterized by the working capacity.The frost resistance of the watergel explosive samples before and after added the antifreeze agent and with different content were tested.The results showed that the performance of the water-gel explosive had been significantly improved after the content of the antifreeze agent reached to 4%.The frost resistance of the water-gel explosive first increased and then decreased as the antifreeze agent increasing,and it showed approximate parabolic pattern and the optimal content of the antifreeze agent was 8%~9%.

关键词(KeyWords)： 水胶炸药;抗冻剂;冷冻;作功能力
Water-gel explosive;Antifreeze agent;Freeze;Working capacity

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 刘飞,郭子如,张阳
LIU Fei,GUO Zi-ru,ZHANG Yang

参考文献(References)：

• 〔1〕汪旭光,聂森林.浆状炸药理论与实践[M].北京:冶金工业出版社,1985:185-232.WANG Xu-guang,NIE Sen-lin.Theory and Practice of Slurry Explosives[M].Beijing:Metallurgical Industry Press,1985:185-232.
• 〔2〕苏晓宁,王瑄,迟道才.混凝土受冻机理及防冻外加剂作用研究[J].混凝土,2004,181(11):22-24.SU Xiao-ning,WANG Xuan,CHI Dao-cai.Research on the Concrete Frost Mechanism and the Antifreezing Admixture Action[J].Concrete,2004,181(11):22-24.
• 〔3〕冯哲,徐会文,展嘉佳.乙二醇复合聚合物抗低温钻井液体系的试验研究[J].世界地质,2008,27(1):95-99.FENG Zhe,XU Hui-wen,ZHAN Jia-jia.Experimental Study on Eth-ylene Alcohol Multiplicity Polymer Drilling Fluid With Low Temperature Resistance[J].Global Geology,2008,27(1):95-99.
• 〔4〕张世杰.低威力水胶炸药[J].煤矿爆破,1995,28(1):37-40.ZHANG Shi-jie.Low Power Water Gel Explosive[J].Coal Mine Blasting,1995,28(1):37-40.
• 〔5〕刘亚松.耐低温水胶震源药柱的研制[J].煤矿爆破,2004,67(4):10-11.LIU Ya-song.The Development of Low Temperature Resistance Type of Seismic Water Gel Explosive[J].Coal Mine Blasting,2004,67(4):10-11.
• 〔6〕黄文尧,颜事龙.炸药化学与制造[M].北京:冶金工业出版社,2009:214-215.HUANG Wen-yao,YAN Shi-long.Explosive Chemical and Manufacturing[M].Beijing:Metallurgical Industry Press,2009:214-215.
• 〔7〕张立.爆破器材性能与爆炸效应测试[M].合肥:中国科学技术出版社,2006:105-142.ZHANG Li.The Performance of Explosive Materials and the Test of Explosion Effect[M].Hefei:China Science and Technology Press,2006:105-142.
• 〔8〕孙跃光.模拟深水装药爆炸作功能力[D].淮南:安徽理工大学,2008.SUN Yue-guang.Study on Power of Explosive Under Simulated Deepwater Explosion[D].Huainan:Anhui University of Science and Technology,2008.